Nikko Steel Kawat Las Elektroda HR-6600 (MMA Electrodes For Hardfacing and Resurfacing - Build Up)

0,00 Rp 0.0 IDR

0,00 Rp

Produk tidak tersedia

Tambah ke Troli

The design emphasis of the flux is designed to ensure a slag solidification range that allows the chrome carbide particles to be evenly distributed within the austenitic alloy matric, so ensuring complete uniformity of hardness.


Jaminan 30-hari uang kembali
Gratis pengiriman di U.S.
Beli sekarang, dapatkan dalam 2 hari.

0

Product Description :

  • The design emphasis of the flux is designed to ensure a slag solidification range that allows the chrome carbide particles to be evenly distributed within the austenitic alloy matric, so ensuring complete uniformity of hardness.

  • The balanced lime rutile flux contains the appropriate alloying elements and is bound with a blend of silicates that ensures both coating strength and resistance to moisture absorption.

Welding Features Of The Electrode :

  • The electrode welds with a smooth stable arc and easily strikes and re-strikes. Weld appearance is bright, almost of polished appearance, smoothly contoured and slag detachability is excellent.

  • The metal recovery is some 170% with respect to core wire weights, thus reducing welding time. The weld deposits are non-machinable.

Applications And Materials To Be Welded :

  • Suitable for surfacing a wide range of steels including 13Mn types. Because thermal contractional stresses will cause stress relieving cross-cracking, buildups should be limited to 3 layers, preferably two when restraint is high.

  • The deposit has excellent resistance to abrasion against minerals, sand and sludges which leads to its extensive use in the earth moving, cement, dredging and steel industries.

  • For build-ups on carbon and low alloy steels or 13Mn steel NSB-307,should be used as a buffer layer.

Specifications for Nikko Steel Kawat Las Elektroda HR-6600 (MMA Electrodes For Hardfacing and Resurfacing - Build Up)

Uk. Elektroda 3.2 mm or 4.0 mm or 5.0 mm