Nikko Steel Kawat Las Elektroda Mo & CrMo Alloyed Heat & Creep Resisting Steels RD-16B

Brosur & Katalog Produk / Brosur & Katalog Produk

Share on Social Networks

Share Link

Use permanent link to share in social media

Share with a friend

Please login to send this document by email!

Embed in your website

Select page to start with

Post comment with email address (confirmation of email is required in order to publish comment on website) or please login to post comment

1. MANUFACTURERS OF A DIVERSE RANGE OF ADVANCED WELDING CONSUMABLES SECTION 5 RD-16B LOW HYDROGEN ELECTRODE FOR WELDING 1.25Cr-0.5Mo STEELS SUBJECTED TO SERVICE AT ELEVATED TEMPERATURES UP TO 550 º C DATA SHEET NO. 48 SPECIFICATION AWS A5.5 BS EN ISO 3580B JIS Z 3223 CLASSIFICATION E8016-B2 E5516-1CM DT2316 PRODUCT DESCRIPTION The design emphasis of the chemically basic flux is engineered to ensure the optimum weld metal properties demanded by the specification are fully met. The basic flux containing the appropriate alloying elements but minimal iron powder, is extruded onto a high purity ferritic core wire and bound with a blend of silicates that ensure both coating strength and a coating resistant to subsequent moisture absorption . WELDING FEATURES OF THE ELECTRODE The chemical nature of the flux together with its controlled coating factor allows the electrode to be used at relatively low amps. This factor together with the fairly fluid but quick freezing slag facilitate vertical up welding including controlled penetration root runs. Overall the arc is very stable, slag detachability is good, fillet welds are slightly convex and metal recovery is some 98% with respect to weight of the core wire. APPLICATIONS AND MATERIALS TO BE WELDED PLATES TO : BS1501: Part 2 Grades 620 and 621 ASTM A387 (pressure vessels) Grades 11 and 12. FORGINGS TO : BS 1503 Grade 620 and 621 CASTINGS TO : BS 1504 Grade 620 and BS3100 Grade B2. ASTM A217 WC6, WC11 PIPES TO : BS3604 Grades 620 and 621. ASTM A335 Grades P11 and P12. ASTM A155 Grades ½Cr and 1¼Cr. A182F11 and F12. TUBES TO : BS3059 Grade 620, ASTM A199, A200 & A213 Grades T11 & T12. HEAT AND CREEP RESISTANCE UP TO 550 º C WHEN WELDING. PRE-HEAT & INTERPASS TEMPERATURES 160 º C MIN AND UP TO 250 º C FOR THICK SECTIONS. WELD METAL ANALYSIS COMPOSITION % BY Wt. C Mn Si S P Cr Mo Fe MIN 0.05 - - - - 1.00 0.40 MAX 0.12 0.90 0.6 0.03 0.03 1.50 0.65 TYPICAL 0.08 0.80 0.3 0.01 0.01 1.25 0.5 Bal. ALL WELD METAL PROPERTIES (AFTER PWHT : 690 ± 15ºC) PROPERTY UNITS MINIMUM TYPICAL OTHERS Tensile strength N/mm 2 550 700 0.2% Proof stress N/mm 2 460 550 Elongation on 4d % 19 24 Reduction of Area (RA) % - 75 Impact energy 0 o C J - 70 H.V. AS WELDED 250 WELDING AMPERAGE AC or DC+ Ø (mm) 2.6 3.2 4.0 5.0 MIN 50 75 130 180 MAX 85 125 170 220 OTHER DATA Electrodes that have become damp should be re-dried at 150 o C for 1 hour RELATED PRODUCTS Please contact our Technical Department for detail. WI-0304 DS48 RD-16B Rev. 3, Date 01.08.2011

Dilihat

  • 153 Total Views
  • 104 Website Views
  • 49 Embeded Views

Tindakan

  • 0 Social Shares
  • 0 Likes
  • 0 Dislikes
  • 0 Comments

Share count

  • 0 Facebook
  • 0 Twitter
  • 0 LinkedIn
  • 0 Google+

Embeds 2

  • 2 sentral.indoteknik.com
  • 7 indoteknikcom.odoo.com